Possible Structure of Surface Active Complexes in Molten CaO-SiO2-CaF2 Slags
Abstract
A section area of silicon and oxygen complexes adsorbed at the boundary of “slag-gas” separation has been calculated in accordance with the concentration dependence of surface tension in molten slags. An assumption on their structure has been made and substantiated. It has been shown that nature of the adsorbed complexes is found to be the same if a slag basicity is more than 1.
About the Authors
V. F Sobolev
Belarusian National Technical University
Belarus
Belarus
A. A. Chichko
Belarusian National Technical University
Belarus
Belarus
References
1. Минаев Ю. А. Поверхностные явления в металлургических процессах. - М.: Металлургия, 1984. - 152 с.
2. Ниженко В. И., Флока Л. И., Хиля Г. П. Состав и свойства двойных металлических расплавов железа, кобальта и никеля с медью // Расплавы. - 1991. - № 5. - С, 111-115.
3. Туркдоган Е. Т. Физическая химия высокотемпературных процессов / Пер. с англ. Ю. И. Уточкина, В. И. Симонова; Под ред. В. А. Григоряна. - М.: Металлургия, 1985.-344 с.
4. Физические свойства расплавов системы СаО- -SіО2 –Al2O3-MgO-CaF2. - М.: Металлургия, 1977.
5. Ejima А., Shimoji М. Effect of alkali and alkaline - earth fluorides on surface tention of molten calcium silicates // Transactions of the Faraday Soc. - 1970. - V. 66, № 565. - P. 99-106.
6. Троцая A. И., Харлашин П. C., Белов Б. Ф. О природе химической связи элементов в металлургических фазах // Изв. вузов. Черная металлургия. - 2002. - № 4. - С. 60-64.
7. Есин О. А., Гельд П. В. Физическая химия пирометаллургических процессов. - М.: Металлургия, 1966.
Review
For citations:
Sobolev V.F., Chichko A.A. Possible Structure of Surface Active Complexes in Molten CaO-SiO2-CaF2 Slags. Science & Technique. 2005;(6):46-49. (In Russ.)
Views:
1363
Email this article 