HARDENING OF CRANE RAILS BY PLASMA DISCRETE-TIME SURFACE TREATMENT

Crane wheels and rails are subjected to intensive wear in the process of operation. Therefore, improvement of these components’ performance can be considered a task of high importance. A promising direction in this regard is surface treatment by highly concentrated energy flows such as laser beams or plasma jets. This thesis suggests that the use of gradient plasma surface treatment can improve the performance of crane rails. A research was conducted, according to which hardened zones were deposited on crane rails under different treatment modes. Microhardness was measured both at the surface and in depth using custom-made microsections. The article includes the results of study of plasma surface hardening effects on wear resistance of crane rails. Change of plasma surface treatment parameters (current, plasma torch movement speed, argon gas flow rate) allows for desired steel hardness and structure, while the choice of optimal location for hardened zones makes it possible to significantly improve wear resistance and crack resistance. As a result of plasma surface hardening, the fine-grained martensite structure is obtained with mainly lamellar morphology and higher hardness rate compared toinduction hardening or overlaying. Wear test of carbon steels revealed that plasma surfacing reduces abrasive wear rate compared to the irinitial state by 2 to 3 times. Enough sharp boundary between hardened and non-hardened portions has a positive effect on the performance of parts under dynamic loads, contributing to the inhibition of cracks during the transition from solid to a soft metal. For carbon and low alloy rail steels, the properties achieved by plasma surface hardening can effectively replace induction hardening or overlaying.The mode range for plasma surface treatment that allow sobtaining a surface layer with certain operating properties has been determined.

1. Petrov S. V. (2005) “Emergency Response” for railways. Mir Tekhniki i Tekhnologiy [World of Technique and Technology], (2), 40-42 (in Russian).

2. Bataev V. A., Bataev A. A., Golkovskii M. G., Ostromenskii P. I., Korotaev B. V. (2002) Lateral edge strengthening of rail heads by electron-beam machining in air. Metallovedenie i termicheskaya obrabotka metallov [Metal science and heat treatment of metals], (12), 14-18 (in Russian).

3. Samotugin S. S., Leshchynski L. K. (2002) Plasma hardening of tool materials. Donetsk, Novy Mir Publ. 383 (in Russian).

4. Lyashenko B. A., Kuzema Yu. A., Digam M. S. (1984) Hardening of metal surfaces by coatings having discrete structure with high adhesive and cohesive resistance. Kiev, Preprint of Institute for Problems of Strength - Academy of Sciences of the Ukrainian Soviet Socialist Republic. 57 (in Russian).

5. Samotugin S. S., Liashenko B. A., Samotugina Iu. S., Gagarin V. A. (2007) Technological fundamentals for deposition of hardening coatings having discrete structure on cast iron products. Nauchnye problemy sovremennoi metallurgii: sb. nauch. tr. [Scientific problems of modern metallurgy. Collection of scientific papers]. Mariupol, Pryazovskyi State Technical University, 162-172 (in Russian).

6. Lyashenko B. A., Movshovich A. Ya., Dolmatov A. I. (2001) Hardening coatings having discrete structure. Tekhnologicheskiye Sistemy [Technological Systems], (4), 17-25 (in Russian).

7. Podgaisky M. S. (1992) Thermal reinforcement of rolled products. Metallovedenie i termicheskaya obrabotka metallov [Metal Science and Heat Treatment of Metals], (10), 20-23 (in Russian).

8. Safonov E. N., Druzhinin I. S., Orlova N. V. (2010) Hardening of surface layer in machine parts by plasma arc of direct action. Uprochnyayushchie tekhnologii i pokrytiya [Hardening Technologies and Coatings], (9), 23-29 (in Russian).

9. Ananiev A. M., Korotkov V. A. (2011) Investigations on material durability of crane rails and wheels. Vestnik Mashinostroyeniya [Mechanical Engineering Bulletin], (8), 35-37 (in Russian).

10. Markashova L. I., Grigorenko G. M., Valevich M. L., Petrov S. V. (2005) Specific features of metal surface layer structure in tread bands of railway wheels after plasma treatment. Avtomaticheskaya Svarka [Automatic Welding], (1), 22-25 (in Russian).