STRUCTURE FORMATION OF ALLOYS ON IRON BASIS AFTER LASER ALLOYING

Abstract

The paper is devoted to investigations on influence of laser treatment regimes of gas-thermal and adhesive coatings from self-fluxing powders on iron basis and after melting with modifying plaster on their roughness and phase composition. One of mathematical planning methods that is a complete factor experiment method has been used for investigation of parameters’ influence on micro-geometry of coatings. The executed investigations have made it possible to observe a general regularity which does not depend on a type of alloying plaster: while increasing speed of laser beam relatively to treated part, beam diameter value of Ra parameter is becoming less. Decrease in height of surface irregularities in case of increasing laser beam speed is related with intensification of evaporation processes. An increase in beam diameter diminishes Ra parameter of the surface. This is due to the fact that decrease in power density occurs at high rate of beam defocusing. Overlapping coefficient does not exert a pronounced effect on Ra parameter of fused coatings. While increasing the speed of laser beam relatively to the part structure is transferred from dendrite into supersaturated one with carbide and boride precipitations. It has been established that technological parameters of laser treatment and particularly speed of laser beam influence on coating composition. While increasing the speed up to v5 = 5 × 10–3 m/s amount of chromium has become larger by 1.5-fold that resulted in increase of micro-hardness of the coating from 9.5–10.1 GPa up to 11.04–15.50 GPa.