PLASTIC DEFORMATION OF GRAPHITE WHILE HEATING COMPOSITE POWDERS
Abstract
The paper presents results of graphite surface morphology research and graphite structure improvement (density increase) in nano-coatings of iron alloy powders while making isothermal heating up to 1200 °С and plastic deformation caused by tensile stress due to significant difference in iron and graphite thermal expansion coefficients. Framework structure formation of squeezed graphite on iron-group metal particles makes it possible to obtain composite powders for preparation of erosion-resistant composite materials.
About the Authors
V. N. Kovalevsky
Belarusian National Technical University
A. E. Zhuk
Институт порошковой металлургии НАН Беларуси
I. V. Fomikhina
Belarusian National Technical University
A. V. Kovalevskaya
Belarusian National Technical University
S. V. Grigoriev
Belarusian National Technical University
A. V. Rulkevich
Институт порошковой металлургии НАН Беларуси
References
1. Костиков, В. И. Сверхвысокотемпературные композиционные материалы / В. И. Костиков, А. Н. Варенков. – М. : Интермет Инжиниринг, 2003. – 560 с.
2. Структурообразование карбидокремниевой матрицы в композиции алмаз – карбид кремния / В. Н. Ковалевский [и др.] // Огнеупоры и техническая керамика. – 2005. – № 5 – С. 8–14.
3. Испытания графита на растяжимость и ползучесть при температурах выше 1650° / Мартенс, Х. Е.[ и др.] // Графит как высокотемпературный материал / пер. с англ. ; под ред. Власова К.П. – М. : Мир, 1964. – С. 139–174.
4. Ковалевский, В. Н. Влияние режимов напыления на свойства аморфных углеродных покрытий / В. Н. Ковалевский, Б. Л. Фигурин, К. Б. Фигурин // Вестник БНТУ. – 2003. – № 5. – С. 22–24.
Review
For citations:
Kovalevsky V.N., Zhuk A.E., Fomikhina I.V., Kovalevskaya A.V., Grigoriev S.V., Rulkevich A.V. PLASTIC DEFORMATION OF GRAPHITE WHILE HEATING COMPOSITE POWDERS. Science & Technique. 2011;(6):9-13. (In Russ.)
Views:
1553
Email this article 