satНАУКА и ТЕХНИКАScience & Technique2227-10312414-0392Belarusian National Technical Universitysat-1295Research ArticleМЕТАЛЛУРГИЯ. МЕТАЛЛООБРАБОТКА. МАШИНОСТРОЕНИЕMETALLURGY. МЕТАL WORKING. MECHANICAL ENGINEERINGТрибологические характеристики плоских поверхностей деталей из спеченного материала ПА-ЖГр2 после иглофрезерованияTribological Characteristics of Flat Surfaces of Parts made of Baked ПА-ЖГр2 Material after Needle MillingФельдштейнE. Э.FeldshtejnE. E.

Доктор технических наук, профессор

БаршайИ. Л.BarshajI. L.

Доктор технических наук

КульбицкийВ. Е.KulbitskijV. E.

Инженер

Зеленогурский технический университетПольшаРolitechnikа ZielonogórskaPolandБелорусский национальный технический университетБеларусьBelarusian National Technical UniversityBelarusМинский автомобильный заводБеларусьBelarusian Automobile PlantBelarus200508022005013639Copyright © Фельдштейн E.Э., Баршай И.Л., Кульбицкий В.Е., 20052005Фельдштейн E.Э., Баршай И.Л., Кульбицкий В.Е.Feldshtejn E.E., Barshaj I.L., Kulbitskij V.E.Данная работа распространяется под лицензией Creative Commons Attribution 4.0.This work is licensed under a Creative Commons Attribution 4.0 License.https://sat.bntu.by/jour/article/view/1295

Рассмотрены закономерности формирования обработанной поверхности и ее износостойкость при иглофрезеровании спеченного материала ПА-ЖГр2. Шероховатость обработанной поверхности снижается по мере увеличения подачи и натяга. Поверхность после обработки практически не содержит пор, на ней заметны следы траекторий одиночных иголок и наплывы деформированного металла по их боковым сторонам. Мгновенный и средний коэффициенты трения для различных условий обработки отличаются примерно на 10 %; различия в относительном объемном износе поверхностей в зависимости от условий обработки достигают трех и более раз. Минимальная интенсивность изнашивания поверхностей после иглофрезерования наблюдается при их обработке с минимальными скоростью фрезерования и подачей и максимальным натягом.

The paper considers regularities of machined surface formation and its wear resistance in the process of needle milling of baked ПА-ЖГр2 material. Roughness of the machined surface is reduced as feed and tightness are increased. The surface being machined does not practically have pores and traces of single needle trajectories and rolls of deformed metal along their lateral sides are observed. Instant and average friction coefficients for various machining conditions differ approximately by 10 %, difference in relative solid surface wear is greater by 3 and more fold in accordance with machining conditions. The minimal intensity of surface wear process after needle milling is observed while machining it with minimal milling speed and feed and maximal tightness.

ReferencesZapf Н. Nadelfrasen-Ein neues spanendes Bear- beitungsverfahren // Fertigungstechnik und Betrieb. - 1977. - V. 27. -№ 4. -S . 218-219.Zapf Н. Nadelfrasen-Ein neues spanendes Bear- beitungsverfahren // Fertigungstechnik und Betrieb. - 1977. - V. 27. -№ 4. -S . 218-219.Абугов А. Л. Иглофреза для подготовки поверхности под покрытие // Станки и инструмент. - 1990. - № 10.-С . 19.Абугов А. Л. Иглофреза для подготовки поверхности под покрытие // Станки и инструмент. - 1990. - № 10.-С . 19.Абугов А. Л. Новые области применения иглофрезерования // Станки и инструмент. - 1992. - № 1. - С. 10-11.Абугов А. Л. Новые области применения иглофрезерования // Станки и инструмент. - 1992. - № 1. - С. 10-11.Гавриленко И. Г. Способ плавно-прерывистого иглофрезерования // Станки и инструмент. - 1993. - №4.-С. 23-23.Гавриленко И. Г. Способ плавно-прерывистого иглофрезерования // Станки и инструмент. - 1993. - №4.-С. 23-23.Баршай И. Л. Обеспечение качества поверхности и эксплуатационных характеристик деталей после обработки в условиях дискретного контакта с инструментом. - Мн.: УП «Технопринт», 2003. - 244 с.Баршай И. Л. Обеспечение качества поверхности и эксплуатационных характеристик деталей после обработки в условиях дискретного контакта с инструментом. - Мн.: УП «Технопринт», 2003. - 244 с.

The authors declare that there are no conflicts of interest present.